Cersanit (located in Walbrzych, Poland) will purchase ceramic rollers with the following parameters:
Length [mm] 4135
Outside diameter [mm] 55
Inner diameter [mm] 43
Working temperature range [°C] Up to 1230
Purpose preheating / firing zone / cooling
Roller replacement temperature [°C] 800
Tiles format [mm] 600x600; 600x1200
Tiles thickness [mm] 8
Number of tiles per row [pcs.] 4
Technology glazed gres
TYPE 1 - roller capabele to align the advancment of the tiles inside the kiln, before the material reaches the firing zone.
Material composition: corund, mullite, zirconia
Al2O3 content min 78%
Bulk density 2,85 kg/dm3
Apparent porosity 16%
Absorbed water 5,5%
M.O.E. 20oC >105GPa
Thermal expansion 20-1000oC 6,2*10-6 K-1
Typical use PRE-FIRING
TYPE 2 - roller recommended for the production of large and tjin tiles (ribbed)
Material composition: corund, mullite, zirconia
Al2O3 content 70%
Bulk density 2,80 kg/dm3
Apparent porosity 17%
Absorbed water 6,0%
M.O.E. 20oC >105GPa
Thermal expansion 20-1000oC 5,5*10-6 K-1
Typical use ACC TO REQUIREMENTS / COOLING
Produkty
1. CERAMIC ROLLER TYPE 1 - 50 szt.
2. CERAMIC ROLLER TYPE 2 - 100 szt.
Length [mm] 4135
Outside diameter [mm] 55
Inner diameter [mm] 43
Working temperature range [°C] Up to 1230
Purpose preheating / firing zone / cooling
Roller replacement temperature [°C] 800
Tiles format [mm] 600x600; 600x1200
Tiles thickness [mm] 8
Number of tiles per row [pcs.] 4
Technology glazed gres
TYPE 1 - roller capabele to align the advancment of the tiles inside the kiln, before the material reaches the firing zone.
Material composition: corund, mullite, zirconia
Al2O3 content min 78%
Bulk density 2,85 kg/dm3
Apparent porosity 16%
Absorbed water 5,5%
M.O.E. 20oC >105GPa
Thermal expansion 20-1000oC 6,2*10-6 K-1
Typical use PRE-FIRING
TYPE 2 - roller recommended for the production of large and tjin tiles (ribbed)
Material composition: corund, mullite, zirconia
Al2O3 content 70%
Bulk density 2,80 kg/dm3
Apparent porosity 17%
Absorbed water 6,0%
M.O.E. 20oC >105GPa
Thermal expansion 20-1000oC 5,5*10-6 K-1
Typical use ACC TO REQUIREMENTS / COOLING
Produkty
1. CERAMIC ROLLER TYPE 1 - 50 szt.
2. CERAMIC ROLLER TYPE 2 - 100 szt.
Time limit for receipt of tenders
Wed Sep 02 13:00:00 GMT 2026
Location
Al. Solidarności 36
25-323 Kielce
25-323 Kielce
Category assortment
Machines, equipment and spare parts
Buyer details
Cersanit S.A.
Al. Solidarności 36
25-323 Kielce
NIP: 5640001666
Al. Solidarności 36
25-323 Kielce
NIP: 5640001666